**Titanium Alloy Plate**
Our titanium alloy plates come in a wide range of thicknesses, from 0.3mm to 200mm, with widths varying from 40mm up to 3500mm. Lengths can be customized to meet your needs, typically ranging from 2000mm to 12000mm. We comply with various international standards including ASTM, JIS, AISI, GB, DIN, and EN. Surface finishes available include BA, 2B, NO.1, NO.4, 4K, HL, and 8K. Our production techniques include both cold rolled and hot rolled options.
Below is a detailed breakdown of our product specifications:
| Standard | Grade | Element Content (wt%) | Mechanical Properties |
|------------|----------|-----------------------|-----------------------------|
| ASTM/ASME | Pure Ti | N≤0.03%, C≤0.08%, H≤0.015%, Fe≤0.2%, O≤0.18% | Strength ≥240 MPa, Ductility ≥24% |
| | Gr.1 | TA1 | |
| | Gr.2 | TA2 | Strength ≥345 MPa, Ductility ≥20% |
| | Gr.3 | TA3 | Strength ≥450 MPa, Ductility ≥18% |
| | Gr.4 | TA4 | Strength ≥550 MPa, Ductility ≥15% |
|------------|----------|-----------------------|-----------------------------|
| Titanium Alloys | Gr.5 | TC4, Ti-6Al-4V | AI: 5.5-6.75%, V: 3.5-4.5 | Strength ≥895 MPa, Ductility ≥10% |
| | Gr.7 | TA9 | Pd: 0.12-0.25 | Strength ≥345 MPa, Ductility ≥20% |
| | Gr.9 | TC2 | AI: 2.5-3.5, V: 2.0-3.0 | Strength ≥620 MPa, Ductility ≥15% |
| | Gr.11 | TA9-1 | Pd: 0.12-0.25 | Strength ≥240 MPa, Ductility ≥24% |
| | Gr.23 | TC4 ELI | AI: 5.5-6.5 | Strength ≥828 MPa, Ductility ≥10% |